In this study, the emulsifying and foaming properties of a novel exudate gum from Dorema ammoniacum (AMG) were assessed in comparison with the well-known gum Arabic from Acacia tree (GAC). The sunflower oil-based emulsion (10% v/v) containing various concentrations (5%–15% w/v) of AMG and GAC was prepared. At all concentrations, AMG showed higher surface and interface activity than GAC. Increasing in AMG and GAC concentrations caused to increase and decrease in Z average, respectively. Overall, the GAC-stabilized emulsion showed lower Z average and PDI value than the AMG-stabilized emulsion during storage time. The sample containing AMG showed higher emulsion capacity and lower emulsion stability in comparison with the one containing GAC at all concentrations. The storage stability decreased and increased with increasing in AMG and GAC concentrations, respectively. After two-week storage, the emulsions containing 10 and 15% AMG showed higher phase separation than those containing GAC; however, this was opposite about sample containing 5% AMG. At thermal, centrifuge, and freezing conditions, the emulsion containing 5% AMG indicated significantly higher stability than GAC samples; however, at higher concentration, opposite effect could be observed. The foaming capacity of the samples containing AMG increased from 81% to 93% by increasing gum concentration from 5% to 15%. The solutions containing AMG showed higher foam capacity than control samples (without gum) and those containing GAC at all concentrations. Increasing in AMG and GAC concentrations slightly improved foam stability, and the highest value (92%) belonged to 15% AMG solution.

The emulsifying and foaming properties of Amuniacum gum (Dorema ammoniacum) in comparison with gum Arabic / Ebrahimi, Behzad; Homayouni Rad, Aziz; Ghanbarzadeh, Babak; Torbati, Mohammadali; Falcone, Pasquale M.. - In: FOOD SCIENCE & NUTRITION. - ISSN 2048-7177. - ELETTRONICO. - early view:(2020), pp. 1-15. [10.1002/fsn3.1658]

The emulsifying and foaming properties of Amuniacum gum (Dorema ammoniacum) in comparison with gum Arabic

Pasquale M. Falcone
Writing – Review & Editing
2020-01-01

Abstract

In this study, the emulsifying and foaming properties of a novel exudate gum from Dorema ammoniacum (AMG) were assessed in comparison with the well-known gum Arabic from Acacia tree (GAC). The sunflower oil-based emulsion (10% v/v) containing various concentrations (5%–15% w/v) of AMG and GAC was prepared. At all concentrations, AMG showed higher surface and interface activity than GAC. Increasing in AMG and GAC concentrations caused to increase and decrease in Z average, respectively. Overall, the GAC-stabilized emulsion showed lower Z average and PDI value than the AMG-stabilized emulsion during storage time. The sample containing AMG showed higher emulsion capacity and lower emulsion stability in comparison with the one containing GAC at all concentrations. The storage stability decreased and increased with increasing in AMG and GAC concentrations, respectively. After two-week storage, the emulsions containing 10 and 15% AMG showed higher phase separation than those containing GAC; however, this was opposite about sample containing 5% AMG. At thermal, centrifuge, and freezing conditions, the emulsion containing 5% AMG indicated significantly higher stability than GAC samples; however, at higher concentration, opposite effect could be observed. The foaming capacity of the samples containing AMG increased from 81% to 93% by increasing gum concentration from 5% to 15%. The solutions containing AMG showed higher foam capacity than control samples (without gum) and those containing GAC at all concentrations. Increasing in AMG and GAC concentrations slightly improved foam stability, and the highest value (92%) belonged to 15% AMG solution.
2020
File in questo prodotto:
Non ci sono file associati a questo prodotto.

I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/11566/282482
 Attenzione

Attenzione! I dati visualizzati non sono stati sottoposti a validazione da parte dell'ateneo

Citazioni
  • ???jsp.display-item.citation.pmc??? ND
  • Scopus 15
  • ???jsp.display-item.citation.isi??? 12
social impact