The present work aims at studying the tensile behavior and formability of pre‐painted steel sheets. To this purpose, uniaxial tensile and hemispherical punch tests were performed in order to analyze the deformation behavior of pre‐painted sheets under uniaxial stretching and biaxial balanced stretching conditions, respectively. Tests were interrupted in order to obtain different strain levels until fracture; at each strain level reached, the occurrence of superficial damages on the paint coating was detected; thinning of the different layers of the pre‐painted sheet was also measured. It was observed that the degree of damage on the paint coating depends on the loading condition; in particular, under uniaxial stretching, the paint coating is able to follow the steel sheet during deformation up to the onset of the necking, whilst, under biaxial balanced stretching, coating exhibits superficial damages before fracture of the sheet.

Tensile behavior and formability of pre‐painted steel sheets / Forcellese, A.; Mancia, T.; Simoncini, M.. - In: METALS. - ISSN 2075-4701. - ELETTRONICO. - 10:1(2020), pp. 53-66. [10.3390/met10010053]

Tensile behavior and formability of pre‐painted steel sheets

Forcellese A.;Mancia T.;Simoncini M.
2020-01-01

Abstract

The present work aims at studying the tensile behavior and formability of pre‐painted steel sheets. To this purpose, uniaxial tensile and hemispherical punch tests were performed in order to analyze the deformation behavior of pre‐painted sheets under uniaxial stretching and biaxial balanced stretching conditions, respectively. Tests were interrupted in order to obtain different strain levels until fracture; at each strain level reached, the occurrence of superficial damages on the paint coating was detected; thinning of the different layers of the pre‐painted sheet was also measured. It was observed that the degree of damage on the paint coating depends on the loading condition; in particular, under uniaxial stretching, the paint coating is able to follow the steel sheet during deformation up to the onset of the necking, whilst, under biaxial balanced stretching, coating exhibits superficial damages before fracture of the sheet.
2020
File in questo prodotto:
Non ci sono file associati a questo prodotto.

I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/11566/275400
 Attenzione

Attenzione! I dati visualizzati non sono stati sottoposti a validazione da parte dell'ateneo

Citazioni
  • ???jsp.display-item.citation.pmc??? ND
  • Scopus 2
  • ???jsp.display-item.citation.isi??? 1
social impact