The creep response in the air of commercially pure titanium was investigated at 550, 600, and 650 °C to assess the effect of oxidation on the mechanical response. Experiments demonstrated that prolonged exposures at high temperatures produced a marked reduction in the minimum creep rate under a given applied stress. Microhardness measurements showed that a hardened zone formed in proximity to the surface due to oxygen penetration into the metal. A simplified composite model was then used to describe the creep response. In this model, the sample consisted of two zones, the hard case that was enriched in oxygen and the soft pure-titanium core, both creeping with similar strain rates. Calculations led to an estimation of the dependence of the minimum creep rate on stress and temperature for the hard high-oxygen zone. The simplified composite model presented here provided a good description of the experimental creep data for pure titanium, tested in its air, and a reliable picture of the effect of oxidation on complex Ti alloys.

Oxidation Effects on Short-Term Creep Response in Air of Commercially Pure Titanium (CP-2 Ti) / Regev, M.; Santoni, A.; Spigarelli, S.. - In: METALS. - ISSN 2075-4701. - 13:7(2023). [10.3390/met13071275]

Oxidation Effects on Short-Term Creep Response in Air of Commercially Pure Titanium (CP-2 Ti)

Santoni A.;Spigarelli S.
2023-01-01

Abstract

The creep response in the air of commercially pure titanium was investigated at 550, 600, and 650 °C to assess the effect of oxidation on the mechanical response. Experiments demonstrated that prolonged exposures at high temperatures produced a marked reduction in the minimum creep rate under a given applied stress. Microhardness measurements showed that a hardened zone formed in proximity to the surface due to oxygen penetration into the metal. A simplified composite model was then used to describe the creep response. In this model, the sample consisted of two zones, the hard case that was enriched in oxygen and the soft pure-titanium core, both creeping with similar strain rates. Calculations led to an estimation of the dependence of the minimum creep rate on stress and temperature for the hard high-oxygen zone. The simplified composite model presented here provided a good description of the experimental creep data for pure titanium, tested in its air, and a reliable picture of the effect of oxidation on complex Ti alloys.
2023
File in questo prodotto:
Non ci sono file associati a questo prodotto.

I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/11566/324692
 Attenzione

Attenzione! I dati visualizzati non sono stati sottoposti a validazione da parte dell'ateneo

Citazioni
  • ???jsp.display-item.citation.pmc??? ND
  • Scopus 1
  • ???jsp.display-item.citation.isi??? 1
social impact