The study is devoted to heavily drawn multicore Cu–18Nb composites of cylindrical and rectangular shapes. The composites were fabricated by the melt-and-deform method, namely, 600 in situ rods of Cu–18%Nb alloy were assembled in a copper shell and cold-drawn to a diameter of 15.4 mm (e = 10.2) and then rolled into a rectangular shape the size of 3 × 5.8 mm (e = 12.5). The specimens were analyzed from the viewpoints of their microstructure, microhardness, and thermal stability. The methods of SEM, TEM, X-ray analysis, and microhardness measurements were applied. It is demonstrated that, at higher strain, the fiber texture ⟨110⟩Nb∥ ⟨111⟩Cu∥ DD (drawing direction), characteristic of this material, becomes sharper. The distortions of niobium lattice can be observed, namely, the {110} Nb interplanar distance is broadened in longitudinal direction of specimens and compacted in transverse sections. The copper matrix lattice is distorted as well, though its distortions are much less pronounced due to its recrystallization. Evolution of microstructure under annealing consists mainly in the coagulation of ribbon-like Nb filaments and in the vanishing of lattice distortions. The structural changes in Nb filaments start at 300–400 °C, then develop actively at 600 °C and cause considerable decrease of strength at 700–800 °C.

Microstructural Features in Multicore Cu–Nb Composites / Elena N., Popova; Irina L., Deryagina; Evgeniya G., Valova-Zaharevskaya; Ruello, Maria Letizia; Vladimir V., Popov. - In: MATERIALS. - ISSN 1996-1944. - ELETTRONICO. - 14:22(2021). [10.3390/ma14227033]

Microstructural Features in Multicore Cu–Nb Composites

Ruello Maria Letizia
Writing – Original Draft Preparation
;
2021-01-01

Abstract

The study is devoted to heavily drawn multicore Cu–18Nb composites of cylindrical and rectangular shapes. The composites were fabricated by the melt-and-deform method, namely, 600 in situ rods of Cu–18%Nb alloy were assembled in a copper shell and cold-drawn to a diameter of 15.4 mm (e = 10.2) and then rolled into a rectangular shape the size of 3 × 5.8 mm (e = 12.5). The specimens were analyzed from the viewpoints of their microstructure, microhardness, and thermal stability. The methods of SEM, TEM, X-ray analysis, and microhardness measurements were applied. It is demonstrated that, at higher strain, the fiber texture ⟨110⟩Nb∥ ⟨111⟩Cu∥ DD (drawing direction), characteristic of this material, becomes sharper. The distortions of niobium lattice can be observed, namely, the {110} Nb interplanar distance is broadened in longitudinal direction of specimens and compacted in transverse sections. The copper matrix lattice is distorted as well, though its distortions are much less pronounced due to its recrystallization. Evolution of microstructure under annealing consists mainly in the coagulation of ribbon-like Nb filaments and in the vanishing of lattice distortions. The structural changes in Nb filaments start at 300–400 °C, then develop actively at 600 °C and cause considerable decrease of strength at 700–800 °C.
2021
File in questo prodotto:
Non ci sono file associati a questo prodotto.

I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/11566/293644
 Attenzione

Attenzione! I dati visualizzati non sono stati sottoposti a validazione da parte dell'ateneo

Citazioni
  • ???jsp.display-item.citation.pmc??? ND
  • Scopus 6
  • ???jsp.display-item.citation.isi??? 6
social impact