Large-area graphitic films, produced by an advantageous technique based on spraying a graphite lacquer on glass and low-density polyethylene (LDPE) substrates were studied for their thermoresistive applications. The spray technique uniformly covered the surface of the substrate by graphite platelet (GP) unities, which have a tendency to align parallel to the interfacial plane. Transmission electron microscopy analysis showed that the deposited films were composed of overlapped graphite platelets of different thickness, ranging from a few tens to hundreds of graphene layers, and Raman measurements provided evidence for a good graphitic quality of the material. The GP films deposited on glass and LDPE substrates exhibited different thermoresistive properties during cooling-heating cycles in the -40 to +40 °C range. Indeed, negative values of the temperature coefficient of resistance, ranging from -4 × 10-4 to -7 × 10-4 °C-1 have been observed on glass substrates, while positive values varying between 4 × 10-3 and 8 × 10-3 °C-1 were measured when the films were supported by LDPE. These behaviors were attributed to the different thermal expansion coefficients of the substrates. The appreciable thermoresistive properties of the graphite platelet films on LDPE could be useful for plastic electronic applications.
Thermoresistive properties of graphite platelet films supported by different substrate / Palomba, M.; Carotenuto, G.; Longo, A.; Sorrentino, A.; Di Bartolomeo, A.; Iemmo, L.; Urban, F.; Giubileo, F.; Barucca, G.; Rovere, M.; Tagliaferro, A.; Ambrosone, G.; Coscia, U.. - In: MATERIALS. - ISSN 1996-1944. - ELETTRONICO. - 12:21(2019), p. 3638. [10.3390/ma12213638]
Thermoresistive properties of graphite platelet films supported by different substrate
Barucca G.;
2019-01-01
Abstract
Large-area graphitic films, produced by an advantageous technique based on spraying a graphite lacquer on glass and low-density polyethylene (LDPE) substrates were studied for their thermoresistive applications. The spray technique uniformly covered the surface of the substrate by graphite platelet (GP) unities, which have a tendency to align parallel to the interfacial plane. Transmission electron microscopy analysis showed that the deposited films were composed of overlapped graphite platelets of different thickness, ranging from a few tens to hundreds of graphene layers, and Raman measurements provided evidence for a good graphitic quality of the material. The GP films deposited on glass and LDPE substrates exhibited different thermoresistive properties during cooling-heating cycles in the -40 to +40 °C range. Indeed, negative values of the temperature coefficient of resistance, ranging from -4 × 10-4 to -7 × 10-4 °C-1 have been observed on glass substrates, while positive values varying between 4 × 10-3 and 8 × 10-3 °C-1 were measured when the films were supported by LDPE. These behaviors were attributed to the different thermal expansion coefficients of the substrates. The appreciable thermoresistive properties of the graphite platelet films on LDPE could be useful for plastic electronic applications.I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.