In the prospect of reducing CO2 emissions and landfilling of waste materials, the preparation of sustainable mortars by alkali activation was studied. According to EN 1504-3:2005, geopolymeric and cementitious mortars belonging to different strength classes (R1 ≥ 10 MPa, R2 ≥ 15 MPa and R3 ≥ 25 MPa) were tested and compared. Geopolymers were obtained with fly ash or metakaolin and a blend of sodium silicate and NaOH (or KOH). Mortars were tested in terms of workability, dynamic modulus of elasticity, drying and restrained shrinkage and porosimetry. Durability was also investigated in terms of water vapour permeability, capillary water absorption and corrosion of possible embedded rebars during the curing period and wet-dry cycles in 3.5% NaCl solution. Results showed that geopolymers are subjected to higher drying shrinkage but lower restrained shrinkage than cementitious mortars. Water vapour permeability was higher in geopolymers and capillary water absorption was lower especially in fly ash geopolymers than those of cementitious mortars. During the first month, the high alkalinity of geopolymers extends the active state of both black and galvanized steel bars. However, when exposed to chlorides, fly ash geopolymers offer a higher protection to reinforcements than cementitious mortars.

Geopolymeric and cementitious mortars with the same mechanical strength class: performances and corrosion behaviour of black and galvanized steel bars / Mobili, Alessandra; Giosue', Chiara; Belli, Alberto; Bellezze, Tiziano; Tittarelli, Francesca. - ELETTRONICO. - (2015), pp. 1-9.

Geopolymeric and cementitious mortars with the same mechanical strength class: performances and corrosion behaviour of black and galvanized steel bars

MOBILI, ALESSANDRA;GIOSUE', CHIARA;Belli, Alberto;BELLEZZE, Tiziano;TITTARELLI, Francesca
2015-01-01

Abstract

In the prospect of reducing CO2 emissions and landfilling of waste materials, the preparation of sustainable mortars by alkali activation was studied. According to EN 1504-3:2005, geopolymeric and cementitious mortars belonging to different strength classes (R1 ≥ 10 MPa, R2 ≥ 15 MPa and R3 ≥ 25 MPa) were tested and compared. Geopolymers were obtained with fly ash or metakaolin and a blend of sodium silicate and NaOH (or KOH). Mortars were tested in terms of workability, dynamic modulus of elasticity, drying and restrained shrinkage and porosimetry. Durability was also investigated in terms of water vapour permeability, capillary water absorption and corrosion of possible embedded rebars during the curing period and wet-dry cycles in 3.5% NaCl solution. Results showed that geopolymers are subjected to higher drying shrinkage but lower restrained shrinkage than cementitious mortars. Water vapour permeability was higher in geopolymers and capillary water absorption was lower especially in fly ash geopolymers than those of cementitious mortars. During the first month, the high alkalinity of geopolymers extends the active state of both black and galvanized steel bars. However, when exposed to chlorides, fly ash geopolymers offer a higher protection to reinforcements than cementitious mortars.
2015
Durability and Sustainability of Concrete Structures ACI SP-305
978-1-942727-44-6
File in questo prodotto:
Non ci sono file associati a questo prodotto.

I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/11566/228051
 Attenzione

Attenzione! I dati visualizzati non sono stati sottoposti a validazione da parte dell'ateneo

Citazioni
  • ???jsp.display-item.citation.pmc??? ND
  • Scopus 13
  • ???jsp.display-item.citation.isi??? ND
social impact