Magnesium alloy sheets are usually obtained by complex processing cycles including hot rolling operations. Temperature of the final stage of rolling strongly affects the microstructure and, consequently, the hot formability of the sheets. In this framework, the present work aims at investigating the effect of the rolling temperature on the hot formability of the innovative magnesium alloy ZAM100. To this purpose, two different rolling temperatures were used and hot formability was investigated by tensile tests performed in extended ranges of temperature and strain rate. The flow curves were analyzed in order to obtain constitutive models of hot formability.

Effect of the Rolling Temperature on Hot Formability of ZAM100 Magnesium Alloy / El Mehtedi, Mohamad; Dorazio, Alessio; Forcellese, Archimede; Pieralisi, Massimiliano; Simoncini, Michela. - ELETTRONICO. - 67:(2018), pp. 493-497. [10.1016/j.procir.2017.12.250]

Effect of the Rolling Temperature on Hot Formability of ZAM100 Magnesium Alloy

Forcellese, Archimede;Simoncini, Michela
2018-01-01

Abstract

Magnesium alloy sheets are usually obtained by complex processing cycles including hot rolling operations. Temperature of the final stage of rolling strongly affects the microstructure and, consequently, the hot formability of the sheets. In this framework, the present work aims at investigating the effect of the rolling temperature on the hot formability of the innovative magnesium alloy ZAM100. To this purpose, two different rolling temperatures were used and hot formability was investigated by tensile tests performed in extended ranges of temperature and strain rate. The flow curves were analyzed in order to obtain constitutive models of hot formability.
2018
Procedia CIRP
File in questo prodotto:
Non ci sono file associati a questo prodotto.

I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/11566/257103
 Attenzione

Attenzione! I dati visualizzati non sono stati sottoposti a validazione da parte dell'ateneo

Citazioni
  • ???jsp.display-item.citation.pmc??? ND
  • Scopus 5
  • ???jsp.display-item.citation.isi??? 4
social impact