Poor interlayer bonding can lead to early failures and thus to a reduction in service life of bituminous pavements. For this reason, it is important to identify the parameters influencing the interlayer shear failure and to characterize their effect by means of laboratory test. In particular, this study is focussed on the effects of test temperature and deformation rate on the interlayer shear strength (ISS) of double-layered asphalt concrete specimens. First, the ISS was measured at temperatures ranging from 0 °C to 30 °C and deformation rates ranging from 0.5 mm/min to 9 mm/min using the Ancona Shear Testing Research and Analysis (ASTRA) device. Then the experimental data were analyzed using a two-stage statistical modelling approach. In the first stage, the variation of ISS versus deformation rate, at each testing temperature, was modelled using both a power-law and a logarithmic function. In the investigated range of deformation rate, the models allowed to estimate the mean ISS with residual standard error varying from 0.062 MPa to 0.128 MPa. Moreover, the linear regression coefficients, which measure the influence of the deformation rate on ISS, changed with temperature. In the second stage, both temperature and deformation rate were used as joint predictors of ISS by using an approach based on the superposition of their effects. Results showed that the time–temperature superposition approach is applicable and a sigmoid-shaped master curve for ISS was obtained. The proposed approach was validated by using ISS measurements obtained on the same materials with different test devices.

Shear failure characterization of time-temperature sensitive interfaces / Canestrari, Francesco; Ferrotti, Gilda; Graziani, Andrea. - In: MECHANICS OF TIME-DEPENDENT MATERIALS. - ISSN 1385-2000. - STAMPA. - 20:3(2016), pp. 405-419. [10.1007/s11043-016-9299-7]

Shear failure characterization of time-temperature sensitive interfaces

CANESTRARI, FRANCESCO
Conceptualization
;
FERROTTI, Gilda
Writing – Original Draft Preparation
;
GRAZIANI, Andrea
Writing – Review & Editing
2016-01-01

Abstract

Poor interlayer bonding can lead to early failures and thus to a reduction in service life of bituminous pavements. For this reason, it is important to identify the parameters influencing the interlayer shear failure and to characterize their effect by means of laboratory test. In particular, this study is focussed on the effects of test temperature and deformation rate on the interlayer shear strength (ISS) of double-layered asphalt concrete specimens. First, the ISS was measured at temperatures ranging from 0 °C to 30 °C and deformation rates ranging from 0.5 mm/min to 9 mm/min using the Ancona Shear Testing Research and Analysis (ASTRA) device. Then the experimental data were analyzed using a two-stage statistical modelling approach. In the first stage, the variation of ISS versus deformation rate, at each testing temperature, was modelled using both a power-law and a logarithmic function. In the investigated range of deformation rate, the models allowed to estimate the mean ISS with residual standard error varying from 0.062 MPa to 0.128 MPa. Moreover, the linear regression coefficients, which measure the influence of the deformation rate on ISS, changed with temperature. In the second stage, both temperature and deformation rate were used as joint predictors of ISS by using an approach based on the superposition of their effects. Results showed that the time–temperature superposition approach is applicable and a sigmoid-shaped master curve for ISS was obtained. The proposed approach was validated by using ISS measurements obtained on the same materials with different test devices.
2016
File in questo prodotto:
Non ci sono file associati a questo prodotto.

I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/11566/238105
 Attenzione

Attenzione! I dati visualizzati non sono stati sottoposti a validazione da parte dell'ateneo

Citazioni
  • ???jsp.display-item.citation.pmc??? ND
  • Scopus 11
  • ???jsp.display-item.citation.isi??? 9
social impact