Single wall carbon nanohorns as well as their thermally oxidized derivatives were decorated with Pd nanoparticles and their H2 sorption performance was examined at 298 K up to 20 bar. The specific surface area of the nanohorns was increased through air oxidation, while both the thermal treatment and the metal doping led to the enhancement of the H2 uptake. The higher uptake of the hybrid materials could not be attributed only to the additive effect of the carbon support and Pd content suggesting the existence of a cooperative mechanism between the metal particles and the carbon surface. This weak chemisorption process was found to be fully reversible after mild heating; still, its contribution to the overall H2 uptake was not found to be of great significance.

Hydrogen storage properties of Pd-doped thermally oxidized single wall carbon nanohorns / Giasafaki, D.; Charalambopoulou, G.; Tampaxis, C. h.; Gattia, D. Mirabile; Montone, A.; Barucca, Gianni; Steriotis, T. h. .. - In: JOURNAL OF ALLOYS AND COMPOUNDS. - ISSN 0925-8388. - ELETTRONICO. - 645:1(2015), pp. 485-489. [10.1016/j.jallcom.2014.12.076]

Hydrogen storage properties of Pd-doped thermally oxidized single wall carbon nanohorns.

BARUCCA, Gianni;
2015-01-01

Abstract

Single wall carbon nanohorns as well as their thermally oxidized derivatives were decorated with Pd nanoparticles and their H2 sorption performance was examined at 298 K up to 20 bar. The specific surface area of the nanohorns was increased through air oxidation, while both the thermal treatment and the metal doping led to the enhancement of the H2 uptake. The higher uptake of the hybrid materials could not be attributed only to the additive effect of the carbon support and Pd content suggesting the existence of a cooperative mechanism between the metal particles and the carbon surface. This weak chemisorption process was found to be fully reversible after mild heating; still, its contribution to the overall H2 uptake was not found to be of great significance.
2015
File in questo prodotto:
Non ci sono file associati a questo prodotto.

I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/11566/221916
 Attenzione

Attenzione! I dati visualizzati non sono stati sottoposti a validazione da parte dell'ateneo

Citazioni
  • ???jsp.display-item.citation.pmc??? ND
  • Scopus 11
  • ???jsp.display-item.citation.isi??? 11
social impact